PLA+

Industrial high performance

PLA+ is our industrial high-quality PLA that offers extreme performance on speed, mechanical properties and high heat environments.
Compared to other high temperature resistant PLA types, PLA+ has the USP of negligible small shrinkage after annealing. With print speeds >120 mm/s you can create more in less time. Objects that are printed with PLA+ will have a semi matte finish which not only looks great but helps concealing layer lines. Do you want an easy to print filament with high mechanical properties for your industrial application? PLA+ will surely charm you!
  • Engineered for fast printing (>120mm/s)
  • Prints like PLA, performs like ABS
  • Great heat resistance at higher temperatures
  • HDT after annealing 95°C+

Available colors for PLA+

Check the availability of your desired color. You’ll find an overview of all ICE Filaments-colors by clicking the button below. Please contact us when your desired color is not available.

Request a custom color

Properties of PLA+

Size ø tolerance Roundness
1.75mm ± 0,05mm ≥ 95%
2.85mm ± 0,10mm ≥ 95%
Description Test Method Typical Value
Specific Gravity ISO 1183 MFI 210°C/2,16kg
MFI 210°C/2,16kg ISO 1133 6g/10 min (Viscosity is lower (higher MFI) at a higher printing temperature (240°C ±10°C), which increases the printing speed capabilities)
Tensile strength ISO 527 39 Mpa
Elongation at break ISO 527 58%
Tensile Modulus ISO 527 3900 Mpa
Impact strength – Charpy notched 23°C ISO 179 22 kJ/m²
Description Test Method Typical Value
Printing temperature ICE Filaments 220 – 250°C (based on speed)
Melting temperature 190 – 220°C
Heat deflection temp. (after annealing) ISO 75 95°C+ (These results are preliminary and are based on several tests made in-house. Current values should be considered factual.)

Additional information and FAQ’s on PLA+